POLYURETHANE BASED ADHESIVE
Chemical Structure: It is a two-component, polyurethane-based adhesive.
Usage Areas: Metal-Metal, Metal-Wood, Wood-Wood, Metal-Styrofoam, tile-
It is used in the bonding process of tiles and similar materials, after 1 day
cures and forms inseparable structures.
Technicial Specifications :
Viscosity(Brookfield) cP : 30.000- 35.000 cP
Color : Cream
Density (gr/cm3): 1.40-1.60
Mixing ratio: 1/5

Flash Point: Above 200 0C
Mixture Usage Time: 15-20 min.
Touch time determination 1.5 hours
Dust free determination 3 hours
Dry touch time determination 2 hours
Determination of hard drying time 5 hours
Final curing 24 hours
Working Method: MT- METALPOLY and MT- METAL with hardener in a container
Put the HEARTER at a ratio of 1/5 and mix thoroughly. Then paste every 2
It is done by rubbing on the surface.
Note: All surfaces must be dry, free from dust, rust and oil before application.
required. To be used within a maximum of 20 minutes after mixing the two substances.
otherwise it will harden and become unusable.
ADVANTAGES OF THE PRODUCT
1) Except for use as an adhesive, in all kinds of materials (plastic
It is also used as an isolation chemical,
2) Provides a solid, unbreakable adhesion,
3) Temperature resistance: Between -40 C and + 80 0C

TECHNICIAL SPECIFICATIONS :
Salt fog test (EN ISO 9227): 800 hours resistance,
Humidity test ( EN ISO 6270-1 ): 800 hours resistance,
UV Resistance test ( EN ISO 4892-2 ): 800 hours resistance,
.
Chemical resistance test (EN ISO 2812-1): 336 hours resistance,
a) No problem with water resistance
b) Resistance to 10% hydrochloric acid, no problem,
c) 10% sodium hydroxide resistance, no problem,
d) Resistance to pure diesel, no problem,
Considerations:
The normal usage mixture of the product is 5 scales of MT- METALPOLİ and 1 scale of METAL
It's HEARTER. It is recommended that the temperature be 18-23 0C during application. Freezing
time depends on ambient temperature. The freezing time is shortened when the environment is warmer.
Packaging : 30 kg. main material
6 kg. hardener
Stocking : + 10 ; + 40 C